Brand

Abrasive castable for flow recycling furnace

Unshaped refractories for “ W”flame power boiler

F-XNJ-90

F-XNJ-80

F-HGJ-80

F-HGJ-90

F-HGK-40

Al2O3         %

90

80

80

90

40

CCS     MPa

110 ℃ ,24h ≥

90

85

20

40

20

815 ℃ ,3h ≥

-

-

30

30

15

1000 ℃ ,3h ≥

90

85

-

-

-

MOR    MPa

110 ℃ ,24h ≥

12

10

5

6

5

815 ℃ ,3h ≥

-

-

6

4

3

1000 ℃ ,3h ≥

15

14

-

-

-

BD    g/ cm3

110 ℃ ,24h ≥

2.90

2.70

2.50

2.60

2.00

LC       %

110 ℃ ,24h ≥

0 ～－ 0.2

0 ～－ 0.2

0 ～－ 0.7

0 ～－ 0.4

0 ～－ 0.2

1000 ℃ ,3h ≥

0 ～＋ 0.4

0 ～＋ 0.4

0 ～＋ 0.1

0 ～＋ 0.5

0 ～＋ 0.5

APPLICATIONS

 The products is used for  refractories .

PACKING

 in 25kg /bag then 40bags  into 1mt big bag or 880bags into container

STORAGE  AND SHELF LIFE

  At least 18 months in dry conditions

AVAILABILITY

 100-1000 metric tons per month

SHIPMENT

 60 days after L/C date

Name

-

L-ladle castable

M,S-ladle castable

Stainless steel fiber reinforced castable

Clay bonded castable

corundum

High-Al

Brand

-

-

-

KIP

GL

A-85

A-70

NL2

NL1

NN

Al2O3     %

≥

90

75

95

94

85

70

65

60

55

MgO        %

4 ～ 8

≥ 10

-

-

-

-

-

-

-

Refractoriness   ℃

≥

-

-

1790

1790

1790

1790

1730

1730

1710

BD        g/ cm3

≥

3.0

2.8

3.1

3.0

2.6

2.6

2.3

2.25

2.25

MST         ℃

-

-

-

1700

1700

1650

1600

1450

1450

1350

CCS   MPa

110 ℃ ,24h

≥

35

25

55

45

40

30

10

3

2

1000 ℃ ,3h

≥

25

20

-

-

-

-

-

-

-

1300 ℃ ,3h

≥

40

40

-

-

-

-

-

-

-

1500 ℃ ,3h

≥

50

50

60

50

45

40

( 1300 ℃ ×3h) ± 0.5

-

-

1650 ℃ ,3h

≥

60

-

-

-

-

-

-

( 1300 ℃ ×3h) ± 0.5

-

LC   %

110 ℃ ,24h

-

-

-

± 0.1

± 0.1

± 0.1

± 0.1

-

-

-

1500 ℃ ,3h

-

-

± 0.8

0 ～＋ 1.0

0 ～＋ 1.0

0 ～＋ 1.0

0 ～＋ 1.0

-

-

( 1300 ℃ ×3h) ± 0.5

1650 ℃ ,3h

-

＋ 0.2 ～＋ 0.4

-

-

-

-

-

-

-

-

MOR MPa

110 ℃ ,24h

≥

4.0

4.0

6.0

5.0

5.0

5.0

2.0

0.5

0.4

1400 ℃ ,0.5h

≥

7.0

-

7.0

6.0

5.0

5.0

-

-

-

APPLICATIONS

The products is used for  refractories .

PACKING

in 25kg /bag then 40bags  into 1mt big bag or 880bags into container

STORAGE  AND SHELF LIFE

At least 18 months in dry conditions

AVAILABILITY

100-1000 metric tons per month

SHIPMENT

 60 days after L/C date

Brand

-

F-ZL-D

F-ZL-G

F-ZL-A

F-ZL-L

Al2O3           %

≥

50

60

-

-

Al2O3+MgO       %

≥

-

-

90

-

Al2O3+MgO+Cr2O3   %

≥

-

-

-

90

BD    g/

110°C,16h

≥

2.30

2.45

3.0

3.0

1350°C,3h

≥

2.25

2.40

3.0

3.0

MOR    MPa

110°C,16h

≥

6

6

5

5

1350°C,3h

≥

9

9

12

12

CCS     MPa

110°C,16h

≥

30

30

30

30

1350°C,3h

≥

50

60

90

90

LC       %

110°C,16h

±

0.2

0.2

-

-

1350°C,3h

±

1.0

1.0

-

-

SST       ℃

-

1600

1600

-

-

Water      %

-

7 ～ 9

7 ～ 9

4.8 ± 0.5

4.8 ± 0.5

application

-

Permanent linings for tundish and ladle

Ladle bottom ,around well block and E.A.F joint

APPLICATIONS

The products is used for  refractories .

PACKING

in 25kg /bag then 40bags  into 1mt big bag or 880bags into container

STORAGE  AND SHELF LIFE

At least 18 months in dry conditions

AVAILABILITY

100-1000 metric tons per month

SHIPMENT

 60 days after L/C date

Brand

-

F-CGL

1

2

3

5

6

8

SiO2           %

≥

28

26

90

75

15

28

MgO             %

≥

52

56

-

10

65

57

C                %

≤

-

5

-

3

5

-

Grain   size ,mm

≤

6

6

6

6

6

6

APPLICATIONS

The products is used for  refractories .

PACKING

in 25kg /bag then 40bags  into 1mt big bag or 880bags into container

STORAGE  AND SHELF LIFE

At least 18 months in dry conditions

AVAILABILITY

100-1000 metric tons per month

SHIPMENT

 60 days after L/C date

brand

-

F-Ⅰ type

F-Ⅱ type

Al2O3           %

≥

97-98

97-98.5

TiO2            %

≤

1.0

0.8

SiO2             %

≤

0.40

0.35

Fe2O3           %

≤

0.20

0.15

T · C               %

≤

0.15

0.10

BD               g/ cm3

≥

3.80

3.85

AP               %

≤

3.5

3.0

Scattering rate    %

≤

1.0

0.5

Grain size,calcined sand

8 -5mm    5 -3mm    3 -1mm    1 -0mm    1 -0.5mm    0.5 -0mm

Fine powder

180f      200f      240f      325f

APPLICATIONS

The products is used for  refractories .

PACKING

in 25kg /bag then 40bags  into 1mt big bag or 880bags into container

STORAGE  AND SHELF LIFE

At least 18 months in dry conditions

AVAILABILITY

100-1000 metric tons per month

SHIPMENT

 60 days after L/C date

APPLICATIONS

The products is used for  refractories .

PACKING

in 25kg /bag then 40bags  into 1mt big bag or 880bags into container

STORAGE  AND SHELF LIFE

At least 18 months in dry conditions

AVAILABILITY

100-1000 metric tons per month

SHIPMENT

 60 days after L/C date

Brand

index

F-DCL-45

F-DCL-50

F-DCL-55

MST               ℃

1450

1450

1450

Refractoriness        ℃

1750

1750

1750

CCS   MPa

110 ℃ ,after drying

500 ℃ ,after heating

1000℃,after heating

≥55

≥55

≥50

≥80

≥80

≥80

≥70

≥70

≥70

Modulus of rupture   MPa

110 ℃ ,after drying

500 ℃ ,after heating

1000℃,after heating

≥8

≥7

≥6

≥10

≥10

≥10

≥10

≥10

≥10

Linear change rate   %

500 ℃ ,after heating

1000℃ ,after heating

1500℃,after heating

-

± 0.5

-0.7

-

± 0.1

± 0.05

± 0.01

± 0.1

-

Chemical composition %

Al2O3

SiO2

Fe2O3

≥ 45

40-45

≤1.2

≥ 40

40-45

≤1.5

≥ 55

35-40

≤1.5

Thermal conductivity rate W/ m · k

800℃

1200℃

≤0.9

≤0.1

≤1.3

≤1.5

≤1.4

≤1.6

Thermal shock resistance ,times

-

-

≥ 40

APPLICATIONS

The products is used for  refractories .

PACKING

in 25kg /bag then 40bags  into 1mt big bag or 880bags into container

STORAGE  AND SHELF LIFE

At least 18 months in dry conditions

AVAILABILITY

100-1000 metric tons per month

SHIPMENT

 60 days after L/C date